Compositions and particles containing cellulosic fibers and stabilized- and/or activated- urease inhibitors, as well as methods of making and using the same

ABSTRACT

The present invention relates to compositions containing stabilized and/or activated urease inhibitors, as well as methods of making and using the same.

The present application claims the benefit of priority under 35 USC §119(e) to U.S. Provisional Patent Application 60/931,682, filed May 23, 2007, which is hereby incorporated, in its entirety, herein by reference.

FIELD OF THE INVENTION

The present invention relates to compositions containing stabilized and/or activated urease inhibitors, as well as methods of making and using the same.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1: Pulp making process indicating addition points therein for the compositions of the present invention.

FIG. 2: Results of room temperature degradation studies of PPDA on pulp.

FIG. 3: Results of aging studies of pulp samples.

FIG. 4: Results of aging studies of treated sheets.

FIG. 5: Results of on shelf aging studies of PPDA treated pulp.

FIG. 6: Results of aging studies of pulp samples in zip lock bag.

DETAILED DESCRIPTION OF THE INVENTION

The inventors have found compositions containing cellulosic fibers and stabilized- and/or activated-urease inhibitors.

The composition of the present invention may contain at least one urease inhibitor. The urease inhibitor may be any chemical or mixtures of chemicals that are capable of inhibiting, preventing, and/or reducing the tendency of a urease protein to degrade urea. Ureases are well known proteins produced by microorganisms to break down and/or degrade urea and/or modified ureas. Examples of ureases, the microorganisms that produce ureases, as well as urease inhibitors can be found in “Improving Efficiency of Urea Fertilizers by Inhibition of Soil Urease Activity” by S. Kiss and M. Simihaian which was published in 2002 by Kluwer Academic Publishers, but are not limited to those described in this reference. Further examples of urease inhibitors can be found in U.S. Pat. Nos. 4,539,037 and 6,828,014; PCT Published Patent Application WO 98/26808; United States Patent Application Publications 2006/0029567 and 2007/0077428, which are all hereby incorporated, in their entirety, herein by reference.

Further examples of urease inhibitors include organic and inorganic compounds. Examples of inorganic compounds include boron compounds, fluorides, and sulfur compounds. Examples of organic compounds include, organo boron acid compounds, hexamethylenetetramine, urea derivatives, dithiocarbamates, thiuram disulfides, sulfides, xanthates, hydroxamic acids such as the mono and di-hydoxamic acids, maleimides, maleic hydrazide, mucochloric acid, bromo-nitro compounds, heterocyclic sulfur compounds, phosphorus containing compounds and phospohorothioate containing compounds, phosphoromonoamidates, phosphorodiamidates, thiophosphorodiamidates, phenylphosphorodiamidate (PPDA), polyphosphorodiamides, phosphorodiamidic acid esters, diamidophosphorothiolates, diamidothiophosphorothiolates, phosphoric triamides, thiophophoric triamides, N-alkylated phosphoric triamide, cyclohexyl phosphoric triamide, N-butyl phosphoric triamide, N-butyl thiophosphoric triamide, and any mixture thereof.

By “alkylated” used above, the urease inhibitor contains an alkyl group. The alkyl group may be of any number of carbon atoms and may be further modified by an amine, hydroxyl, ester, ether, and/or carboxyl/carbonyl functionality. Preferably, the alkyl group is not modified and contains from 1 to 12 carbon atoms, more preferably from 1 to 6 carbon atoms. Further, the alkyl group may be a methyl, ethyl, N-propyl, isopropyl, N-butyl, iso-butyl, tert-butyl, pentyl, cyclopentyl, hexyl, and cyclohexyl group. Accordingly, the alkyl group may be cyclic and/or may be aromatic.

Preferred phosphorodiamidates include phenylphosphorodiamidate (PPDA). Preferred N-alkylated phosphoric triamides include cyclohexyl phosphoric triamide and N-butyl phosphoric triamide. Preferred N-alkylated thiophosphoric triamides include N-butyl thiophosphoric triamide (NBTP).

The composition may contain the at least one urease inhibitor at any amount, including from 0.05 ppm to 10 wt %, preferably from 1 ppm to 2 wt %, more preferably from 5 ppm to 5,000 ppm, most preferably from 10 to 1500 ppm of the at least one urease inhibitor based upon the total weight of the composition.

The composition of the present invention may contain at least one stabilizer. In this sense the stabilizer preferably stabilizes the urease inhibitor when present in the composition. Examples of stabilizers include, but are not limited to alkylene oxides such as those having from 2 to 6 carbon atoms, polyalkylene oxides such as those having from 2 to 6 carbon atoms, polyethylene oxides, ethylene oxides, propylene oxides, polypropylene oxides, diethylene oxides, dipropylene oxides, glycerin, diypropylene glycol, ethylene glycol, polypropylene glycol, substituted ethylene glycols such as methoxyethylene glycols, ethylene glycol ethers such as ethylene glycol monobutyl ether and ethylene glycol monoethyl ether.

The stabilizer may have any melting temperature (T_(m)). In one embodiment the stabilizer may be a liquid at room temperature and have a melting temperature that is not more than room temperature. In another embodiment, the stabilizer may be in the form of a solid at room temperature and have a melting temperature that is at least room temperature, preferably from room temperature to 125° C., more preferably at least 60° C.

The composition may contain the at least one stabilizer at any amount, including from 0.1 to 99.99 wt % based upon the total weight of the composition, preferably from 0.1 to 10 wt % based upon the total weight of the composition, more preferably from 0.1 to 5 wt % based upon the total weight of the composition.

The composition may contain at least one activator. The activator may include hindered amines such as those having the following chemical formula:

where R₀ is a —O⁻ radical, —OH, —O-phenyl, —O-alkyl preferably substituted or unsubstituted having from 1 to 6 carbon atoms, and —H; where R₁ is hydrogen, oxo, hydroxy, acetoamido, or phosphonooxy groups. The activators may be 2,2,6,6-tetramethyl piperidine and derivatives thereof, 2,2,6,6-Tetramethylpiperidine-1-oxyl (TEMPO), 4-hydroxy2,2,6,6-Tetramethylpiperidine-1-oxyl(4-hydroxy TEMPO), 4-oxy-TEMPO, 4-acetamido-TEMPO, 4-phosphonooxy-TEMPO, N-hydroxybenzotriazole, N-hydroxymaleimide, N-hydroxysuccinamide, N-hydroxyphthalimide, hydroxybenzothiazole, oxa-benzotrazole, d- and aza-pyridine-triazole, violuric acid, and UV absorbers based on benzotriazole, as well as mixtures thereof. Further, any one of these activators may be used in combination with any oxidant and/or oxidative enzyme. Examples of oxidants are perborates and percarbonates. An example of an oxidative enzyme is lacasse (examples of reductases).

The composition may contain the at least one activator at any amount, including from 1 ppm to 10 wt %, preferably from 100 ppm to 10 wt %, more preferably from 0.1 wt % to 10 wt %, based upon the total weight of the composition.

The composition of the present invention may also contain at least one inert substance. Examples of inert substances may include, but is not limited to, dessicants, talc, talc powder, stearates, calcium stearate, stearic acid, palmitates, zeolites, calcium chloride, calcium carbonate, ammonium chloride, anhydrous silica, calcium silicates, aluminosilicates such as Hydrex, diatomaceous earth, phosphates, sodium phosphate, potassium phosphates, ammonium phosphates, calcium phosphates, hydroxyapatite, superabsorbent polymers, polyvinyl polypyrrolidone (PVPP), alumina, silica, and mixtures thereof. Preferable inert substances include those having moisture barrier forming compounds and moisture absorbing compound. Examples of moisture absorbing compounds are dessicants.

If the inert particle is a superabsorbent particle, the superabsorbent particle may be of any size and shape such as a powder, a fiber, or a disk. In one embodiment, the superabsorbent particle may be not greater than 1000 microns, preferably not greater than a 100 microns.

The composition may contain the at least one inert substance at any amount, including from 0.1 to 10 wt % based upon the total weight of the composition.

The composition of the present invention may also contain at least one preservative. Examples of the preservative include, but is not limited to, parabens, polyparaben, benzoates, benzoate esters, phenolsulfonic acids, and mixtures thereof

The composition of the present invention may contain at least one cellulosic fiber. Examples of the cellulosic fiber include fiber derived from hardwood trees, softwood trees, or a combination of hardwood and softwood trees prepared for use in a papermaking furnish and/or fluff pulp furnish by any known suitable digestion, refining, and bleaching operations. The cellulosic fibers may be recycled fibers and/or virgin fibers. Recycled fibers differ from virgin fibers in that the fibers have gone through the drying process at least once. In certain embodiments, at least a portion of the cellulose/pulp fibers may be provided from non-woody herbaceous plants including, but not limited to, kenaf, hemp, jute, flax, sisal, or abaca although legal restrictions and other considerations may make the utilization of hemp and other fiber sources impractical or impossible. Either bleached or unbleached pulp fiber may be utilized in the process of this invention. High yield pulps and/or mechanical pulps such as TMP, CMP, and BCTMP are also included as the cellulosic fiber of the present invention.

Preferably, the sources of the cellulose fibers are from softwood and/or hardwood species. In one embodiment the source is softwood. In another embodiment, the source is at least 50 wt %, sometimes at least 95 wt %, softwood based upon the total weight of the fibers.

The composition of the present invention may contain the cellulosic fiber at any amount, including at least 60 wt % cellulosic fibers, preferably at least 70 wt %, more preferably at least 80 wt %, most preferably at least 90 wt %, based upon the total weight of the composition.

Further, the cellulosic fibers, preferably softwood and/or hardwood cellulosic fibers, contained by the composition of the present invention may be modified by physical and/or chemical means. Examples of physical means include, but is not limited to, electromagnetic and mechanical means. Means for electrical modification include, but are not limited to, means involving contacting the fibers with an electromagnetic energy source such as light and/or electrical current. Means for mechanical modification include, but are not limited to, means involving contacting an inanimate object with the fibers. Examples of such inanimate objects include those with sharp and/or dull edges. Such means also involve, for example, cutting, kneading, pounding, impaling, etc means.

Examples of chemical means include, but is not limited to, conventional chemical fiber modification means including crosslinking and precipitation of complexes thereon. Examples of such modification of fibers may be, but is not limited to, those found in the following patents U.S. Pat. Nos. 6,893,473; 6,592,717, 6,592,712, 6,582,557, 6,579,415, 6,579,414, 6,506,282, 6,471,824, 6,361,651, 6,146,494, H1,704, 5,731,080, 5,698,688, 5,698,074, 5,667,637, 5,662,773, 5,531,728, 5,443,899, 5,360,420, 5,266,250, 5,209,953, 5,160,789, 5,049,235, 4,986,882, 4,496,427, 4,431,481, 4,174,417, 4,166,894, 4,075,136, and 4,022,965, which are hereby incorporated, in their entirety, herein by reference. Further modification of fibers is found in United States Patent Publication Numbers 20060185808; 20060260773; 20070051481; 20070119556; 20070193707; 20070277947; and 20080066878 which are hereby incorporated, in their entirety, herein by reference.

The cellulosic fiber may also be in the form of fines. Sources of “Fines” may be found in SaveAll fibers, recirculated streams, reject streams, waste fiber streams. The amount of “fines” present in the composition can be modified by tailoring the rate at which such streams are added to the papermaking process and/or fluff pulp making process.

In one embodiment, any of the above-mentioned fibers may be treated so as to have a high ISO brightness. Examples of such fibers treated in this manner include, but is not limited to, those described in United States Patent Publication Number 2006-0185808; U.S. patent application Ser. No. 11/445,809 entitled “Pulp and Paper Having Increased Brightness” filed Jun. 2, 2006; and U.S. patent application Ser. No. 11/446,421 entitled “IMPROVED PROCESS FOR MANUFACTURING PULP, PAPER AND PAPERBOARD PRODUCTS” filed Jun. 2, 2006; which are hereby incorporated, in their entirety, herein by reference. The fiber may have any brightness, including at least 80, at least 85, at least 90, and at least 95 Iso Brightness.

The cellulosic fiber may have any brightness and/or CIE whiteness. Examples of measuring CIE whiteness and obtaining such whiteness in a fiber and paper made therefrom can be found, for example, in U.S. Pat. No. 6,893,473, which is hereby incorporated, in its entirety, herein by reference.

The composition may or may not contain water. In one embodiment, the composition may contain at least one cellulosic fiber, at least one urease inhibitor, at least one stabilizer and preferably substantially no water. In another embodiment, the composition may contain at least one cellulosic fiber, at least one urease inhibitor, at least one activator, and optionally water.

In one embodiment of the present invention, the composition may contain at least one cellulosic fiber, at least one urease inhibitor, and at least one polymer having a melting temperature of from room temperature to 125° C. Preferably, the polymer is also a stabilizer as discussed above. The composition may or may not contain water, but preferably contains substantially no water. The composition may contain a superabsorbent particle. When the composition contains a superabsorbent particle, the superabsorbent particle may have any particle size. Preferably, the particle size of the superabsorbent particle is not more than 100 microns. Preferably, the composition itself is in the form of a particle. More preferably, the polymer provides a coating on the at least one cellulosic fiber. Even more preferably, the urease inhibitor and optionally the superabsorbent particle are present in the polymeric coating of the at least one cellulosic fiber.

In one particular embodiment, when at least one urease inhibitor and at least one cellulosic fiber is present in the composition of the present invention, it is preferred that from 0.5 ppm to 10 wt % of the urease inhibitor is present based upon the total amount of the cellulosic fiber. When at least one stabilizer, at least one urease inhibitor, and at least one cellulosic fiber is present in the composition of the present invention, it is preferred that from 0.1 to 20 wt % of the stabilizer is present based upon the total amount of the cellulosic fiber. When at least one activator, at least one urease inhibitor, and at least one cellulosic fiber is present in the composition of the present invention, it is preferred that from 1 ppm to 10 wt % of the activator is present based upon the total amount of the cellulosic fiber. When at least one inert substance, at least one urease inhibitor, at least one cellulosic fiber and optionally at least one stabilizer and/or optionally at least one activator are present in the composition of the present invention, it is preferred that from 0.1 to 10 wt % of the inert substance is present based upon the total weight of the composition.

The composition of the present invention may also contain optional compounds such as optical brightening agents, whiteners, biocides, enzymes, and starch.

The composition of the present invention may be made by any conventional manner of contacting or mixing at least one urease inhibitor with at least one stabilizer and/or at least one activator mentioned above; optionally at least one inert substance, and optionally at least one cellulosic fiber. The at least one urease inhibitor may be serially, consecutively, and/or simultaneously contacted with at least one stabilizer and/or at least one activator mentioned above; optionally at least one inert substance, and optionally at least one cellulosic fiber.

The above contacting may occur at any temperature. In one embodiment, the contacting is performed at a temperature that is greater than the melting temperature of the stabilizer such that at least the urease inhibitor is dissolved in the stabilizer. Subsequently, the resultant composition may be cooled, preferably to room temperature.

In one embodiment, the a composition containing the urease inhibitor and the stabilizer is contacted with at least one surface of a web of fiber. The composition may be applied to the entire surface of at least one side of the web of just a fraction or portion thereof.

In one embodiment, at least one urease inhibitor is mixed with at least one stabilizer and/or at least one activator; and optionally at least one inert substance to form the composition. Then, this mixture may be contacted with at least one cellulosic fiber. This contacting may occur at any conventional stage during the papermaking or fluff pulp making processes. FIG. 1 depicts these general processes and provides preferable contact points, i.e. 1-6, in which the mixture is contacted with at least one cellulosic fiber. Preferable contact points during this general process are those points depicted as 2-11 in FIG. 1. Most preferable contact points during this general process are those points depicted as 3-11 in FIG. 1. In addition, the contacting may occur by any general method of contacting a mixture with at least one cellulosic fiber such as spraying, curtain coating, coating, roll coating, knife coating, blade coating, size press coating etc. General coating methods may be those mentioned and described in textbooks such as those described in the “Handbook for pulp and paper technologists” by G. A. Smook (1992), Angus Wilde Publications, which is hereby incorporated, in its entirety, by reference. Preferred methods of contacting include coating methods such as liquid spraying, hot-melt spraying, liquid curtain coating and hot-melt curtain coating. More preferred methods of contacting include hydraulic nozzle spraying, atomizing spraying, electrostatic spraying, and hot-melt spraying. The most preferred method of contacting include hydraulic spraying and hot melt spraying.

When the urease inhibitor and the stabilizer are first contacted within one another prior to application to the fiber, the concentrations of the urease inhibitor and the stabilizer may be any concentrations, including from 0.1 to 10 wt %, 0.5 to 7 wt %, 1 to 5 wt %, and 2 to 4 wt %, based upon the total weight of the urease inhibitor and the stabilizer of so long as the concentrations are such that the urease inhibitor has improved stability prior to contacting with the fiber. These concentrations are applicable when the urease inhibitor and the stabilizer are contacted in solid and/or liquid form such that urease inhibitor is dissolved and/or encapsulated by the stabilizer. Again, the concentrations may be much higher when the urease inhibitor and stabilizer are contacted, such as instances in the solid state or in instances forming emulsions, suspensions, colloids, and the like.

In another embodiment, when the composition contains at least one urease inhibitor mixed with at least one stabilizer and/or at least one activator; and optionally at least one inert substance to form the composition; the composition may be contacted with at least one cellulosic fiber when the fiber is a member of a web of cellulosic fibers. In this case, again any of the above-mentioned contacting methods may be employed such that at least one surface of the web is contacted with the composition. However, the web may have two sides and/or surfaces to it; and, both of these surfaces may be simultaneously or consecutively contacted with the composition by any of the above contacting methods.

When the composition containing at least one urease inhibitor, at least one stabilizer and/or at least one activator, and optionally at least one inert substance is mixed with at least one cellulosic fiber, the weight ratio of the mixture to the cellulosic fiber may be any weight ratio, preferably less than 1:4, more preferably less than 1:9, most preferably less than 1:10. When this mixture is coated onto the cellulosic fiber, any coat weight is acceptable. Preferably, the coat weight is less than 20 wt %, preferably less than 15 wt %, more preferably less than 10 wt %, most preferably less than 5 wt % based upon total weight of the composition including the cellulosic fiber.

After the above-mentioned contacting step, the resulting composition may be optionally dried and/or solidified.

In a particular embodiment, at least one urease inhibitor is contacted with at least one stabilizer optionally in the presence of an inert substance and preferably in substantially no water. The urease inhibitor may or may not be dissolved, but is preferably dissolved, into the at least one stabilizer. This mixture is then contacted with at least one cellulosic material as described above.

In another embodiment, at least one urease inhibitor is contacted with at least one activator in the absence or presence of water. This mixture is then contacted with at least one cellulosic material as described above.

The composition of the present invention is preferably an odor controlling composition. The odor controlling composition may inhibit, prevent, reduce, and/or retard the production of odors in the presence of bodily fluids. Examples of such bodily fluids include urine, urea, blood, menstrual fluid, fecal matter, feces, etc. The composition may control odor caused by the growth of microorganisms in the presence of such bodily fluids. Examples of the microorganisms of interest are those that are able to break down urea into ammonia. In one embodiment, it is most preferable that the composition of the present invention is odor controlling but does not inhibit, prevent, reduce, and/or retard the growth of microorganisms, such as those that are able to breakdown urea into ammonia.

In addition, the composition of the present invention preferably lessons the energy necessary to convert and/or sheer the composition into a fluff pulp product as compared to conventional untreated fluff pulp compositions. In addition, the composition preferably has liquid absorption properties that are not significantly impacted and/or reduced as compared to untreated fluff pulp.

The present invention also relates to an article containing or formed from any of the above-mentioned compositions of the present invention. The article of the present invention is preferably an odor controlling composition. The odor controlling article may inhibit, prevent, reduce, and/or retard the production of odors in the presence of bodily fluids. Examples of such bodily fluids include urine, urea, blood, menstrual fluid, fecal matter, feces, etc. The article may control odor caused by the growth of microorganisms in the presence of such bodily fluids. Examples of the microorganisms of interest are those that are able to break down urea into ammonia. In one embodiment, it is most preferable that the article of the present invention is odor controlling but does not inhibit, prevent, reduce, and/or retard the growth of microorganisms, such as those that are able to breakdown urea into ammonia.

Examples of the article include absorbent articles and fluff pulp. Examples of absorbent articles may include personal hygiene articles and others made of fluff pulp. Examples of personal hygiene articles or products include diapers, fluff pulp, adult incontinence products, feminine hygiene products such as sanitary napkins, etc.

In additional embodiments of the present invention, the compositions and/or articles may be combined with untreated fibers and/or articles that are commonly known. In the case of fibers, treated fibers and compositions containing the same may be contacted, mixed, and/or blended in any way with untreated fibers to produce compositions and/or articles containing a mixture of treated and untreated fibers.

The present invention also relates to a method of reducing the production of ammonia from urea in the presence of at least on microorganism by contacting any one or more of the composition and/or articles mentioned above with urea and at least one microorganism.

The present also relates to a method of reducing the degradation of a urease inhibitor by adding a stabilizer thereto, especially in the presence of a fiber, such that there remains an effective amount of urease inhibitor in the composition and/or article so as to reduce ammonia production when in the presence of urea and at least one microorganism. The suitable time for such a shelf life may be at least one week, at least 4 weeks, at least 6 weeks, at least 15 weeks, at least 18 weeks, at least 28 weeks, and at least 52 weeks. The suitable time may include at least 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 15, 20, 25, 28, 30, 35, 40, 45, 50, 52, 75, 104, 208, and 416 weeks.

As used throughout, ranges are used as a short hand for describing each and every value that is within the range, including all subranges therein.

All of the references, as well as their cited references, cited herein are hereby incorporated by reference with respect to relative portions related to the subject matter of the present invention and all of its embodiments

EXAMPLES Bacterial Ammonia Test

Test Pad Sample Preparation

-   1. Place a non-woven carrier on the 50 mm diameter SCAN pad former     screen, attach tube, tare, and place on SCAN test piece former. -   2. Weigh out 0.60 gm fiberized pulp. Fibers should be “fluffy”, well     dispersed, and spread evenly in the weighing pan. -   3. Sprinkle 0.40 gm SAP evenly over the fiber. -   4. Start the vacuum and feed the SAP/fiber into the forming cone     through the feed tube, ensuring that both materials are     simultaneously introduced. -   5. Remove the pad assembly from the former and weigh. Lightly     compress the pad and remove the tube. -   6. Lift the non-woven carrier with the pad off of the screen. -   7. Press to −3 mm -   8. Seal pad wrapped in non-woven in a plastic ziplok bag until     testing.

Test Solutions Preparation

Synthetic Urine Make-Up

-   -   MgSO4, 0.66 g/750 ml     -   KCl, 4.47 g/750 ml     -   NaCl, 7.6 g/750 ml     -   Urea 18 g/750 ml     -   KH2PO4, 3.54 g/750 ml     -   Na2HPO4, 0.745 g/750 ml

Nutrient Broth

Bacterial Organism and Test Solution Preparation

A broth culture of Proteus mirabilis ATCC #7002 is propagated in AOAC Nutrient Broth at 37+/−2° C. for 24 hours. This 24 hour culture contains ˜10⁹ CFU/ml. The culture is further diluted in a synthetic urine/nutrient mix, to give a final bacterial concentration of ˜10⁸ CFU/ml. The synthetic urine has been supplemented with AOAC Nutrient Broth to give a final concentration of 25%. This is the Test Inoculum Solution.

An aliquot of this solution is serially diluted in AOAC phosphate buffer water. Dilutions of 10⁻⁵′ 10⁻⁶, 10⁻⁷, and 10⁻⁸ are plated to determine actual number of CFU/ml in the Test Inoculum Solution.

The final Test Inoculum Solution composition is:

-   75% synthetic urine -   25% nutrient broth -   10⁸ CFU/ml Proteus mirabilis

Ammonia Measurement

The pad is placed, forming wire side up, into a sterile wide mouth 120 ml septa jar (non-woven carrier removed). The pad is inoculated with 15 ml of the diluted test organism in synthetic urine with 25% AOAC Nutrient Broth, i.e., the Test Inoculum Solution. The jar is sealed and incubated at 35+/−2° C.

At the end of the designated exposure period, the ammonia in the headspace of the sealed jar is measured using the Drager system. The sampling end of the Drager tube is fitted with a needle which is inserted through the septum. A vent needle is inserted to allow withdrawal of the gaseous sample. The opposite end of the measuring tube is attached to the Drager pump. Ammonia is withdrawn according to the manufacturer specifications for the tube and the measurement recorded.

Example 1

Bleached softwood pulp was made into hand-sheets. The hand-sheets were sprayed with a 400 ppm solution of phenyl phosphorodiamidate (PPDA), to have a PPDA content of 400 ppm on the pulp sheets. The sheets were dried with a lab cylinder drier at 195 F.

The PPDA treated pulp was then shredded by a lab hammermill to convert into fluff fibers. The treated fluff fibers were then mixed with 40% by weight of SAP (superabsorbent polymer) particles, and made into pads for subsequent ammonia generation tests with Proteus Mirabilis in synthetic urine. For control, the untreated fluff with 40% SAP was used.

Table 1 shows the test result. It is obvious that the PPDA treated fluff completely prevented any ammonia generation by 8 hrs and 12 hrs tests.

TABLE 1 8 hrs test 12 hrs test % Reduction % Reduction NH3 of treated NH3 of treated concen- fluff against concen- fluff against tration control fluff tration control fluff Fluff treated  0 ppm 100%   0 ppm 100% with 400 ppm PPDA Control - 650 ppm 1025 ppm Untreated fluff

Example 2

Bleached softwood pulp hand sheets were treated with respectively 5 ppm, 50 ppm, 100 ppm and 400 ppm PPDA on the pulp. It was then tested likewise as in Example 1. The result indicated that no ammonia was formed. The % NH3 reduction of treated fluff against untreated fluff, is 100%. No ammonia was generated from any of the treated fluff.

TABLE 2 8 hrs test 12 hrs test % NH3 Reduction % NH3 Reduction of treated of treated fluff against fluff against control fluff control fluff Fluff treated with 6  99%  92% ppm PPDA Fluff treated with 50 100% 100% ppm PPDA Fluff treated with 100 100% 100% ppm PPDA Fluff treated with 400 100% 100% ppm PPDA

Example 3

Bleached softwood pulps that were treated with 400 ppm PPDA was stored on shelf as dry pulp in ambient conditions for 18 weeks and 20 weeks. The aged pulp samples were then fluffed and tested for ammonia generation by bacteria as in Example 1. The result showed that the PPDA inside cellulosic pulp was not stable, and it lost all its effectiveness against ammonia generation in 20 weeks.

TABLE 3 8 hrs test 12 hrs test % NH3 Reduction % NH3 Reduction of treated of treated fluff against fluff against control fluff control fluff Fluff treated with 400 ppm 12% 22% PPDA -- stored for 18 weeks Fluff treated with 400 ppm  0%  3% PPDA --stored for 20 weeks

HPLC chromatography test on the 20 week sample showed no PPDA remaining on the pulp. The 18 week sample had trace amount of PPDA remaining.

Example 4

It is known that PPDA is not stable in water. But dry PPDA is known to be stable.

For this reason, one would expect PPDA treated fluff pulp (which is dry) would have sufficient stability in storage before use (which would be wetted by urine and other aqueous fluids).

However, it was quite a surprise that PPDA, when applied on the cellulose pulp, would degrade very fast as shown by the Table 4 below. In fact, it degraded faster in the dry sheet (although only has 50% humidity in the air), than PPDA dissolved in the water. This can be shown in the FIG. 2.

Therefore, there is a critical need of strategies that may delay or reduce the urease inhibitor degradations. This is one embodiment addressed by the present invention.

TABLE 4 400 ppm PPDA 1000 ppm PPDA in Dry Pulp in Dry Pulp Stored at room Sored at room temperature temperature 1000 ppm PPDA and 50% humidity and 50% humidity Dissolved PPDA PPDA completely in concen- concen- Water at room tration tration temperature Days remaining % remaining % % in in pulp, Degra- in pulp, Degra- Degra- storage ppm dation ppm dation dation 1 5.5% 2 5.3% 3 6.3% 4 6.7% 7 179 55.3% 374 62.6% 9  14% 14 77 80.8% 133 86.7% 21 53 86.8% 95 90.5% 28 28 93.0% 38 96.2% 35 17 95.8% 16 98.4% 42 7 98.3% 7 99.3% 49 2 99.5% 2 99.8% 56 2 99.5% 3 99.7%

Example 5

Bleached softwood pulp sheets were treated (sprayed) respectively with: 1) 400 ppm PPDA on pulp from water solution; 2) 400 ppm PPDA on pulp from PEG-200 solution; 3) 400 ppm PPDA on pulp from solution of 90% PEG-200 and 10% Talc powder. All the samples were dried on a dryer can at 195 F. They were then stored under room temperature (23 C) and 50% humidity chamber. The PPDA content remaining in the dry pulp samples was tested by HPLC.

The results in the figure below showed that PEG, or PEG with talc particles, can all reduce PPDA degradation on dry cellulosic pulps, as compared to the control pulp (treated with PPDA/water and dried).

TABLE 5 Aging at 23 C. and 50% RH 400 ppm PPDA 400 ppm PPDA 400 ppm PPDA on pulp on pulp on pulp from water from PEG from PEG/talc Weeks of aging, PPDA PPDA PPDA 23 C., 50% RH remaining remaining remaining 1 179 2 77 3 53 100 140 4 28 94 53 5 17 43 6 7 7 2

Example 6

We have found that PEG and dipropylene glycol (which we had used as the chemical to reduce the PPDA degradation on pulp) had very little degradation of PPDA, which is also corroborated with our previous finding that PEG could be used to substantially reduce the PPDA degradation on the treated fluff pulp. See Table 6 and FIG. 4.

TABLE 6 Making 2% PPDA Solution in Various Types of Glycols NH3 in headspace, ppm NH3 in headspace, Immediately after ppm 4 days PPDA dissolution in storage Propylene glycol 7.5 110 Poly (propylene glycol) 90 380 Dipropylene glycol 0 35 PEG, polyethylene glycol 0 10

Example 7

PPDA dissolved in PEG has other advantages over PPDA dissolved in water, in the present application for fluff pulp odor control. It is well known that urease inhibitor PPDA has some unpleasant smell by itself.

In the present invention, we discovered that these smells from PPDA can be suppressed by PEG. In fact, PEG may also be used to suppress and mask other malodors in cellulosic fluff pulps and diapers (including odors from urease inhibitors, and/or odors from bodily fluids in use).

In our example, 0.2% PPDA water solution was compared with 0.2% PPDA in PEG solution. In 40 ml vials, 10 ml of each solution was used (therefore 30 ml headspace). Both GC-MS and human smell were conducted. The results below are self-explanatory.

TABLE 7 Other malodorous Phenol in compounds detected by Headspace GC-MS in the headspace by GC-MS (qualitative) Smells 0.2% PPDA 1042 ng/ml Styrene, xylenes, chloro- Strong bitter, in Water phenol, nitro-phenol, rubbery odors di-t-butyl benzene, di-butyl quinine, di-t-butyl phenol, and some C4-C9 ketones 0.2% PPDA  78 ng/ml Peaks not detected, or No obvious in PEG suppressed, or masked. unpleasant odors

Example 8

Bleached softwood pulp sheets were treated (sprayed) respectively with:

-   1) 400 ppm PPDA on pulp from water solution; -   2) 400 ppm PPDA on pulp from solution of 90% water and 10% Talc; -   3) 400 ppm PPDA on pulp from PEG-200 solution; -   4) 400 ppm PPDA on pulp from solution of 90% PEG-200 and 10% Talc     powder; -   5) 400 ppm PPDA on pulp from glycerin solution.

All the samples were dried on a dryer can at 195 F.

They were then put into a controlled chamber with temperature of 55 C and 50% relative humidity. The PPDA content remaining in the dry pulp samples was tested by HPLC.

The results are shown in the table below. Under such conditions of aging in one week, the pulp samples that were treated by PEG, and PEG/Talc still maintain some level of PPDA.

TABLE 8 PPDA remaining on pulp, Treated Pulp Samples, aged 55 C., and 50% RH after one week 400 ppm PPDA on pulp from water solution 0 400 ppm PPDA on pulp from solution of 90% 0 water and 10% Talc 400 ppm PPDA on pulp from PEG-200 solution 12 ppm 400 ppm PPDA on pulp from solution of 90%  7 ppm PEG-200 and 10% Talc powder 400 ppm PPDA on pulp from glycerin solution 0

Example 9

Bleached softwood pulp was treated with 400 ppm NBPT (n-butyl thiophosphoric triamide) on pulp. It was then fluffed, mixed with 40% SAP and tested for ammonia generation by bacteria as in Example 1. In comparison, pulp samples treated with (1) 400 ppm NBPT together with 0.1% 4-hydroxy TEMPO, (2) 400 ppm NBPT with 2.5% hydroxyethyl urea, and (3) pulp treated with 0.1% hydroxyl TEMPO alone were also tested.

It was found that 0.1% TEMPO made the NBPT much more effective in controlling the ammonia generation. TEMPO or TEMPO derivatives were found to be an activator in enhancing the effectiveness of NBPT.

Hydroxyethyl urea was found to be an excellent agent for increasing the solubility of NBPT and PPDA in water (from 0.2%-0.4% concentration, improved to 3%-5% concentrations).

TABLE 9 8 hrs test 12 hrs test % NH3 Reduction % NH3 Reduction of treated of treated fluff against fluff against control fluff control fluff Fluff treated with 400 ppm 82% 53% NBPT Fluff treated with 400 ppm 68% 42% NBPT, together with 2.5% hydroxyl-ethyl urea Fluff treated with 400 ppm 94% 81% NBPT, together with 0.1% hydroxyl TEMPO Fluff treated with 0.1% 29%  0% TEMPO alone

Example 10

One of many objectives of the present invention, is to control odor (ammonia) formation, without killing bacteria. That is, we would not want to have any biocide, or biocidal effect, while suppressing and controlling odor formation from urine or other bodily fluids. However, killing bacteria, via biocidal effect may occur in other embodiments of the present invention.

Here are some examples below. No significant change of bacteria population was observed, while ammonia formation was suppressed. This is also true with our “activators” (such as hydroxyl TEMPO) that enhance the effectiveness of urease inhibitors (such as NBPT).

TABLE 10 After 8 hrs of Inoculum of incubation Proteus (Proteus After 8 hrs mirabilis, mirabilis) NH3 generated ATCC 7002 Average Counts in headspace, Fluff Sample Pads CFU/ml per pulp sample pad ppm Control (untreated 10⁸ 1.3 × 10¹⁰ 733 pulp mixed with 40% SAP) Pulp treated with 10⁸ 2.2 × 10¹⁰ 0 400 ppm PPDA (mixed with 40% SAP) Pulp treated with 10⁸ 1.6 × 10¹⁰ 0 400 ppm PPDA and 0.1% hydroxyl- TEMPO (mixed 40% SAP) Pulp treated with 10⁸ not tested 106 400 ppm NBPT (mixed 40% SAP) Pulp treated with 10⁸ 1.6 × 10¹⁰ 39 400 ppm NBPT and 0.1% hydroxyl- TEMPO (mixed 40% SAP) Special Control 10⁸ 1.2 × 10¹⁰ 326 (untreated pulp mixed with 40% “Odor-Control- SAP”)

Example 11

Accelerated aging study was done at 35 C and 50% RH with individual sheets thoroughly exposed to the environment. The control PPDA doses were 400 ppm and 1000 ppm based on the weight of the sheet, applied with water solution and dried. And the stabilized PPDA doses were also at 400 ppm and 1000 ppm on sheet, applied with 2% PPDA solution in PEG-200. The results are shown in the table below, and plotted in FIG. 4.

TABLE 11 Aging at 35 C. and 50% RH Control Control Stabilized Stabilized 400 ppm 1000 ppm 400 ppm 1000 ppm Weeks of aging PPDA PPDA PPDA PPDA at 35 C., 50% RH Remaining remaining remaining remaining 0 476 1053 399 1093 1 50 74 322 853 2 0 0 119 488 3 123 321 4 57 145 5 28 95 6 11 60

Example 12

Aging test was also conducted on-shelf in the bag at room conditions. The result was shown in Table 12, and plotted in FIG. 5 in log scale.

TABLE 12 On-Shelf Aging Control 400 Stabilized 400 Stabilized 1000 ppm (sheets ppm (sheets ppm (sheets treated with 400 treated with 400 treated with 1000 ppm PPDA on ppm PPDA on ppm PPDA on pulp from water pulp from PEG- pulp from PEG- Weeks on solution and dried) 200 solution) 200 solution) Shelf PPDA on pulp PPDA on pulp PPDA on pulp 0 (applied) 400 400 1000 15 87 403 16 57 380 17 33 387 18 <0.5 28 7

From the results, the control PPDA treated pulp decomposes quickly. On the other hand, with the inventive stabilization composition, the shelf life can be easily extended to beyond half a year (26 weeks). With proper stabilized dose, the shelf life can be expected to extend to 1 year (52 weeks) or beyond as well.

Example 13

As an alternative strategy to Example 10, we may need options to inhibit the growth of various bacterial populations, while preventing ammonia formation through urease inhibition, for multi-odor control. This is especially useful when preventing multiple odors in various bodily fluids such as menstrual fluid, blood, fecal matter, feces, urea and urine. One strategy is to use anti-microbial polymers together with our stabilized urease inhibitors (with or without commonly used absorbents). In this example, PHMB (polyhexamethylene biguanide) in fluff pulp treatment is used for demonstration. It was found that PHMB treated fluff pulp could inhibit bacterial growth, and it was also found to have some odor control functions by itself.

Other antibacterial polymers include various derivatives of PHMB or functional equivalents thereof (such as PEHMB, PHMG, PEEG, BBIT and boric acid_, and those based on quaternary amines, as well as many others such as polynoxylins (a urea-formaldehyde polymer).

TABLE 13 After 8 hrs of Inoculum of incubation Proteus (Proteus After 8 hrs mirabilis, mirabilis) NH3 generated ATCC 7002 Average Counts in headspace, Fluff Sample Pads CFU/ml per pulp sample pad ppm Control (60% 10⁸ 1.9 × 10¹⁰ 860 untreated pulp mixed with 40% SAP) Pulp treated with 10⁸ 5.6 × 10⁸  600 0.5% PHMB (mixed with 40% SAP) Special Control 10⁸ 1.9 × 10¹⁰ 342 (60% untreated pulp mixed with 40% “odor- control-SAP”)

Example 14

There are many commercial products claiming to have odor control functions. Traditionally, odor absorptions or neutralization have been extensively used. Those strategies may only abate the odor molecules within the absorbent capacity. In most cases, the odors are generated over time by urinary tract bacteria, which may quickly go beyond the capacity of the absorbents. Table 14 below shows some of the comparisons of odor control effectiveness among the commercial products, as tested by our method here.

TABLE 14 NH3 generated in headspace after 8 hrs of incubation in synthetic urine inoculated with Samples Proteus mirabilis Control Lab Pad 700 ppm (60% untreated fluff mixed with 40% SAP) Special Lab Pad 400 ppm Control (untreated fluff mixed with 40% “odor-control SAP”) Commercial Brand A-1 480 ppm Commercial Brand A-2 363 ppm Commercial Brand B 700 ppm Commercial Brand C 750 ppm Commercial Brand D 760 ppm Commercial Brand E 780 ppm Commercial Brand F 920 ppm Control Lab Pad 900 ppm (60% untreated fluff mixed with 40% SAP) Fluff treated with  <6 ppm 400 ppm PPDA (stabilized with PEG-200), after aged 14 weeks. (mixed with 40% SAP)

It is shown that the inventive composition and article of the present invention containing stabilized urease inhibitor is substantially more effective than any commercial products tested so far. Brand A-1 and Band A-2, which are relatively more effective than other commercial products, are probably based on “odor-control SAP (superabsorbent polymer)” technologies.

Example 15

All the activators disclosed (including by not limited to tempos, laccase mediators, oxidative enzymes, etc) may have urease inhibition by themselves, as shown by some of our examples. These activators may also be compatible with our stabilized urease inhibitors.

For instance, violuric acid when dissolved in water displays strong pink colors. The pink color can “dye” the pulp as well, especially when metal ions are present. The well-known discoloration by violuric acid, however, can be alleviated by dissolving violuric acid in PEG-200 (non-aqueous) which displays a dim blueish color. The violuric acid in PEG solution is compatible with stabilized urease inhibitors such as PPDA and others.

In general, all the activators can be compatible with the urease inhibitors stabilized by PEG.

Example 16

Solid PEG particles (CartaCoat GP from Clariant) were mixed with 1% by weight of PPDA powders. The solid mixtures were then heated at 80 C until all the PEG melted. After stirring, the molten mixture was then let to cool down into solids.

-   -   The solid blocks stabilized the PPDA, and the blocks can also be         “rubbed” against the moving fluff web as one of the coating         application of the stabilized urease inhibitors.     -   The molten solid may also be made into particles (ground         powders, granules, etc) and/or mixed with SAP particles. Such         particles alone or in combination with SAP particles may be         added to fibers prior to, during, or after during any converting         operation (such as hammermills).

This applies to all stabilized urease inhibitors and activators (and/or other inert particles/absorbents).

Example 17

Storage of treated pulp samples, as prepared in Example 12, inside Zip-Loc plastic bags have slightly improved stability. The results are shown in Table 15, and FIG. 6 below.

TABLE 15 Aging in Zip-Loc Bag on Shelf Stabilized 400 ppm Stabilized 1000 ppm (sheets treated with (sheets treated with 400 ppm PPDA 1000 ppm PPDA on pulp from on pulp from PEG-200 solution) PEG-200 solution) Weeks in Zip-Loc Bag PPDA on Pulp PPDA on Pulp 0 (applied) 400 1000  4 426 15 211 18 209 24 154 27 117 317 33 88 221

Numerous modifications and variations on the present invention are possible in light of the above teachings. It is, therefore, to be understood that within the scope of the accompanying claims, the invention may be practiced otherwise than as specifically described herein. 

What is claimed is:
 1. A composition, comprising at least one cellulosic fiber; at least on urease inhibitor; and at least one member selected from the group consisting of a stabilizer and an activator.
 2. The composition according to claim 1, wherein the composition comprises a stabilizer and does not contain water.
 3. The composition according to claim 1, further comprising an activator and water.
 4. The composition according to claim 1, further comprising an inert substance.
 5. The composition according to claim 1, further comprising a dessicant.
 6. The composition according to claim 1, wherein the urease inhibitor comprises at least one member selected from the group consisting of a n-alkyl phosphoric triamide, n-alkyl thiophosphoric triamide, and a phophoroamidate.
 7. The composition according to claim 1, wherein the at least one urease inhibitor comprises n-butyl thiophosphoric triamide (NBPT), phenyl phosphoroamidate (PPDA), or mixtures thereof.
 8. The composition according to claim 1, further comprising from 0.5 ppm to 10 wt % of the at least one urease inhibitor based upon the total weight of the composition.
 9. The composition according to claim 1, wherein the at least one stabilizer comprises at least one member selected from the group consisting of a polyalkylene oxide.
 10. The composition according to claim 1, wherein the at least one stabilizer comprises polyethylene glycol, glycerin, dipropylene glycol, or mixtures thereof.
 11. The composition according to claim 1, further comprising from 0.1 to 20 wt % of the at least one stabilizer based upon the total weight of the composition.
 12. The composition according to claim 1, wherein the activator comprises at least one member selected from the group consisting of a hindered amine, N-hydroxybenzotriazole, N-hydroxymaleimide, N-hydroxysuccinamide, N-hydroxyphthalimide, hydroxybenzothiazole, oxa-benzotrazole, d- and aza-pyridine-triazole, violuric acid, and UV absorbers based on benzotriazole.
 13. The composition according to claim 1, wherein the at least one activator comprises 2,2,6,6-Tetramethylpiperidine-1-oxyl (TEMPO), 4-hydroxy2,2,6,6-Tetramethylpiperidine-1-oxyl(4-hydroxy TEMPO), or mixtures thereof.
 14. The composition according to claim 1, further comprising from 1 ppm to 10 wt % of the at least one activator based upon the total weight of the composition.
 15. The composition according to claim 1, further comprising at least one inert material.
 16. The composition according, further comprising at least one inert material selected from the group consisting of water absorbing compounds and water barrier forming compounds.
 17. The composition according to claim 1, further comprising at least one inert material wherein the at least one inert material comprises at least one dessicant.
 18. The composition according to claim 1, further comprising at least one inert material wherein the at least one inert material comprises at least one dessicant selected from the group consisting of superabsorbent particles.
 19. The composition according to claim 1, further comprising at least one dessicant wherein the at least one dessicant comprises talc.
 20. The composition according to claim 1, further comprising from 0.1 to 10 wt % of at least one inert material based upon the total weight of the composition.
 21. The composition according to claim 1, further comprising from 0.1 to 10 wt % of at least one dessicant based upon the total weight of the composition.
 22. A method of making the composition according to claim 1, comprising contacting the at least one cellulosic fiber with the at least one urease inhibitor and the at least one member selected from the group consisting of a stabilizer and an activator.
 23. The method according to claim 22, further comprising pre-mixing the at least one urease inhibitor and the at least one member selected from the group consisting of a stabilizer and an activator.
 24. The method according to claim 22, further comprising drying the composition.
 25. The method according to claim 22, wherein the at least on cellulosic fiber is consecutively or simultaneously contacted with at least one urease inhibitor and the at least one member selected from the group consisting of a stabilizer and an activator.
 26. The method of making the composition according to claim 1, comprising contacting a web of cellulosic fibers with the at least one urease inhibitor and the at least one member selected from the group consisting of a stabilizer and an activator.
 27. The method according to claim 26, further comprising pre-mixing the at least one urease inhibitor and the at least one member selected from the group consisting of a stabilizer and an activator.
 28. The method according to claim 26, further comprising drying the composition.
 29. The method according to 26, wherein said contacting is performed by spraying the at least one urease inhibitor and the at least one member selected from the group consisting of a stabilizer and an activator onto at least one surface of the web of cellulosic fibers.
 30. The method according to claim 29, wherein the at least one urease inhibitor and the at least one member selected from the group consisting of a stabilizer and an activator are sprayed simultaneously or consecutively.
 31. An article, comprising the composition according to claim
 1. 32. The article according to claim 31, wherein the article is at least one member selected from the group consisting of an absorbent article and a personal hygiene article.
 33. The article according to claim 31, wherein the article is selected from the group consisting of a diaper, a feminine hygiene article, and an adult incontinency product.
 34. The article according to claim 31, further comprising at least one super absorbent particle.
 35. A method of making the article according to claim 34, comprising contacting at least one super absorbent particle with a composition comprising at least one cellulosic fiber; at least on urease inhibitor; and at least one member selected from the group consisting of a stabilizer and an activator.
 36. A method of inhibiting the production of ammonia from urea in the presence of at least one microorganism, comprising contacting the article according to claim 31 with urea and at least one microorganism.
 37. The method according to claim 36, wherein the growth of the at least one microorganism is not inhibited.
 38. The method according to claim 36, wherein the at least one microorganism is a urease-producing microorganism.
 39. A method of inhibiting the production of ammonia from urea in the presence of at least one microorganism, comprising contacting the composition according to claim 1 with urea in the presence of at least one microorganism.
 40. The method according to claim 39, wherein the growth of the at least one microorganism is not inhibited.
 41. The method according to claim 38, wherein the at least one microorganism is a urease-producing microorganism.
 42. A composition, comprising at least one cellulosic fiber; at least on urease inhibitor at least one super absorbent particle; and a stabilizer having a T_(m) that is from room temperature to 120° C.
 43. The composition according to claim 42, wherein the super absorbent particle has a particle size that is less than 100 microns.
 44. The composition according to claim 42, wherein the composition is a particle.
 45. The composition according to claim 42, wherein the stabilizer coats the at least one cellulosic fiber.
 46. The composition according to claim 42, wherein the stabilizer is at least one member selected from the group consisting of polyalkylene oxides and polyethylene glycol.
 47. The composition according to claim 42, wherein the stabilizer is polyethylene glycol.
 48. The composition according to claim 42, wherein the stabilizer forms a matrix in which the at least on urease inhibitor, the at least one cellulosic fiber, and the at least one super absorbent particle reside.
 49. A method of making the composition according to claim 42, comprising contacting at least one cellulosic fiber with at least one urease inhibitor, at least one super absorbent particle; and a stabilizer having a T_(m) that is from room temperature to 125° C.
 50. The method according to claim 49, wherein the at least one cellulosic fiber is simultaneously or consecutively contacted with at least one urease inhibitor, at least one super absorbent particle; and a stabilizer having a T_(m) that is from room temperature to 125° C.
 51. The method according to claim 49, comprising contacting at least one cellulosic fiber with a mixture comprising at least one urease inhibitor, at least one super absorbent particle; and a a stabilizer having a T_(m) that is from room temperature to 125° C.
 52. The method according to claim 51, wherein the mixture is sprayed onto a web of cellulosic fibers.
 53. The method according to claim 51, wherein the mixture is a liquid and is sprayed onto a web of cellulosic fibers.
 54. The method according to claim 51, wherein the mixture is a liquid.
 55. The method according to claim 51, wherein the mixture is contacted at a temperature that is higher than the Tm of the stabilizer.
 56. The method according to claim 51, further comprising cooling the composition.
 57. The method according to claim 51, further comprising drying the composition.
 58. The method according to claim 51, further comprising mixing the at least one urease inhibitor with at least one super absorbent particle; and a stabilizer having a T_(m) that is from room temperature to 125° C.
 59. The method according to claim 49, further comprising mixing the at least one urease inhibitor with at least one super absorbent particle; and a stabilizer having a T_(m) that is from room temperature to 125° C.
 60. An article, comprising the composition according to claim
 40. 61. The article according to claim 60, wherein the article is at least one member selected from the group consisting of an absorbent article and a personal hygiene article.
 62. The article according to claim 60, wherein the article is selected from the group consisting of a diaper, a feminine hygiene article, and an adult incontinency product.
 63. The article according to claim 60, further comprising at least one super absorbent particle.
 64. A method of making the article according to claim 63, comprising contacting at least one super absorbent particle with a composition comprising at least one cellulosic fiber; at least on urease inhibitor; and at least one member selected from the group consisting of a stabilizer and an activator.
 65. A method of inhibiting the production of ammonia from urea in the presence of at least one microorganism, comprising contacting the article according to claim 60 with urea and at least one microorganism
 66. The method according to claim 65, wherein the growth of the at least one microorganism is not inhibited.
 67. The method according to claim 65, wherein the at least one microorganism is a urease-producing microorganism.
 68. A method of inhibiting the production of ammonia from urea in the presence of at least one microorganism, comprising contacting the composition according to claim 40 with urea in the presence of at least one microorganism.
 69. The method according to claim 68, wherein the growth of the at least one microorganism is not inhibited.
 70. The method according to claim 67, wherein the at least one microorganism is a urease-producing microorganism.
 71. A method, comprising contacting the composition according to claim 42 or the composition according to claim 1 with a fiber to create a mixture of treated and untreated fibers.
 72. The method according to claim 71, further comprising forming the mixture into an article.
 73. The method according to claim 72, wherein the article is an absorbent article 